MOLYKOTE® Anti-Friction Coatings

for Plastic and Plastic/Metal Lubrication

3400 A

View pdf data-sheet

Type AF Coating formulated to prevent corrosion and fretting corrosion. Heat-curing.
Typical applications Hinge bolts, bushings, cams, pins, springs, screw spindles, lock and brake parts.
Properties
  • Excellent corrosion protection
  • Outstanding adhesion on metal
  • Low coefficient of friction
  • Strong resistance against oil and fuels
  • Good pressure resistance
  • Protection against fretting corrosion
  • Wide service temperature range
  • High wear protection
Physical/chemical data
Colour Grey
Composition
  • Solid lubricants
  • Organic binder
  • Solvent
  • Corrosion inhibitor
Temperature
Service temperature range,°C -200 to +430
Flash point, ISO 1523, °C <+ 21
Drying time, 20 °C, min 10-15
Curing time, min/°C 60/200
Load carrying capacity, wear protection, service life
Falex pressure resistance, ASTM-D-2625, N p=20000
Coefficient of friction
LFW-1, ASTM-D-2714, 
Rotating, n=72 rpm, v=7.9 m/min no. of revolutions to µ=0.1 p=85000 (2860 N)
Oscillating, frequency=89.5 osc./min, no. of oscillations to µ=0.08 p=42000 (900 N)
Corrosion protection
Salt spray test, DIN 50021, h 120
Fretting corrosion (Deyber tester) 4.5 · 106
Surface covering capacity, m²/kg 15
Storage life, years 5
Technical data sheet, no. 71-0030-01
Application method Apply a thin, even film by dipping or spraying onto degreased components. Life can be increased by phosphate or sand blast pre-treatment. Optimum film thickness is 15 µm. Cure after evaporation of solvent. Please refer to special literature.
Packages Can: 500 g
Container: 5 kg
Back to Products list